- pearlite transformation
- Смотри перлитное превращение.
Энциклопедический словарь по металлургии. — М.: Интермет Инжиниринг. Главный редактор Н.П. Лякишев. 2000.
pearlite transformation
Смотреть что такое "pearlite transformation" в других словарях:
Pearlite — is a two phased, lamellar (or layered) structure composed of alternating layers of alpha ferrite (88 wt%) and cementite (12%) that occurs in some steels and cast irons. It forms by a eutectoid reaction as austenite is slowly cooled below 727°C.… … Wikipedia
перлитное превращение — [pearlite transformation] превращение переохлажденного аустенита в смесь феррита, почти не содержащего углерода и цементита, содержащего 6,67 % С, при медленном охлаждении или изотермической выдержке ниже Аc1; сопровождатсяе диффузией,… … Энциклопедический словарь по металлургии
steel — steellike, adj. /steel/, n. 1. any of various modified forms of iron, artificially produced, having a carbon content less than that of pig iron and more than that of wrought iron, and having qualities of hardness, elasticity, and strength varying … Universalium
Steel — For other uses, see Steel (disambiguation). The steel cable of a colliery winding tower … Wikipedia
Bainite — is a phase that exists in steel microstructures after certain heat treatments. First described by Davenport E. S. and Edgar Bain, it is one of the decomposition products that may form when austenite (the face centered cubic crystal structure of… … Wikipedia
Carbon steel — Iron alloy phases Ferrite (α iron, δ iron) Austenite (γ iron) Pearlite (88% ferrite, 12% cementite) … Wikipedia
Martensite — For the transformation, see Diffusionless transformations. Iron alloy phases Ferrite (α iron, δ iron) A … Wikipedia
Eutectic point — The melting point of a mixture of two or more solids (such as an alloy) depends on the relative proportions of its ingredients. A eutectic or eutectic mixture is a mixture at such proportions that the melting point is as low as possible, and that … Wikipedia
Austenite — (or gamma phase iron) is a metallic non magnetic solid solution of iron and an alloying element. In plain carbon steel, austenite exists above the critical eutectoid temperature of 1000 K (about 727 °C); other alloys of steel have different… … Wikipedia
Annealing (metallurgy) — Annealing, in metallurgy and materials science, is a heat treatment wherein a material is altered, causing changes in its properties such as strength and hardness. It is a process that produces conditions by heating to above the recrystallization … Wikipedia